Механичка својства
Brass has different mechanical properties due to different zinc content. Fig. 7 is a graph showing the change of mechanical properties of brass with different zinc content. For brass, σb and δ increase with the increase of zinc content. For ( plus ) brass, the strength at room temperature increases continuously before the zinc content increases to about 45 percent . If the zinc content is further increased, the R phase with greater brittleness (solid solution based on Cu5Zn8 compound) appears in the alloy structure, and the strength decreases sharply. The room temperature plasticity of ( plus ) brass always decreases with the increase of zinc content. Therefore, the copper-zinc alloy containing more than 45 percent zinc has no practical value.
Обични месинг се широко користи, као што су појас резервоара за воду, цев за довод воде и одводњавање, медаља, валовита цев, серпентинска цев, кондензаторска цев, кућиште, разни сложени ударни производи, хардвер и тако даље. Са повећањем садржаја цинка са Х63 на Х59, могу добро да издрже врућу обраду, а највише се користе у разним деловима машина и електричних уређаја, делова за штанцање и музичких инструмената.
Да би се побољшала отпорност на корозију, чврстоћа, тврдоћа и обрадивост месинга, мала количина елемената као што су калај, алуминијум, манган, гвожђе, силицијум, никл, олово итд. (углавном 1 проценат 2 процента, неколико до 3 процента 4 процента, и неколико до 5 процената) се додаје легури бакра-цинка да би се формирале тернарне, квартарне или чак квинарне легуре, што је сложено
Еквивалентни коефицијент цинка
The microstructure of complex brass can be calculated according to the "zinc equivalent coefficient" of elements added in brass. Because a small amount of other alloying elements are added to Cu-Zn alloy, the /( plus ) phase region in Cu-Zn state diagram usually moves to the left or right. Therefore, the microstructure of special brass is usually equivalent to that of ordinary brass with increased or decreased zinc content. For example, the microstructure of Cu-Zn alloy with 1 percent silicon is equivalent to the alloy structure with 10 percent zinc added in Cu-Zn alloy. So the "zinc equivalent" of silicon is 10. The "zinc equivalent coefficient" of silicon is the largest, which makes the /( plus ) phase boundary in Cu-Zn system significantly move to the copper side, that is, the phase region is strongly reduced. The "zinc equivalent coefficient" of nickel is negative, that is, the phase region is enlarged.
-Фаза и -фаза у специјалном месингу су сложена вишеелементна чврста раствора, која имају велики ефекат јачања, док -фаза и -фаза у обичном месингу су једноставни Цу{5}}Зн чврсти раствори, који имају мали ефекат јачања. Иако је еквивалент цинка еквивалентан, својства вишекомпонентног чврстог раствора и једноставног бинарног чврстог раствора су различита. Према томе, мала количина више-ојачања је начин да се побољшају својства легуре.